The Effect of Curing Time and Light Intensity on Composite Resin: the Effect of Curing Time and Light Intensity on the Degree of Conversion of Poly-acid Modified Composite Resin
M. G. Al-shaekh
The aims of this study are to investigate the effect of light intensity and curing time on the degree of conversion and amount of residual monomer released from poly-acid modified composite resin samples cured with QTH light curing unit. Single light cured poly-acid modified composite resin restorative material Glasiosite Caps (VOCO/ Cuxhaven, Germany) (n=130 samples divided to the groups ) exposed to different exposure times (10, 30 and 40 seconds) and at different light intensities (410 and 490 mw/cm²). The degree of conversion of poly-acid modified composite resin samples was investigated by Fourier transform infrared spectroscopy (FTIR). While the amount of residual monomer released from poly-acid modified composite resin samples was investigated through measuring the released residual monomer in doubled distilled water with (CECIL 2000) Ultraviolet visible spectrophotometer.
| Mediji | Grāmatas Paperback Book (Grāmata ar mīksto vāku un līmēto muguru) |
| Izlaists | 2011. gada 4. marts |
| ISBN13 | 9783844310009 |
| Izdevēji | LAP LAMBERT Academic Publishing |
| Lapas | 128 |
| Izmēri | 226 × 8 × 150 mm · 209 g |
| Valoda | Vācu |
Skatīt visus M. G. Al-shaekh